In the present investigation V2O5 powders are exposed to biofield. Both the exposed and unexposed powders are later characterized by various techniques. The average particle size is found to decrease with increase in number of days after treatment upto a maximum of 15.9% in 110 days indicating severe fracture at agglomerate/crystallite boundaries. The BET surface area showed a surprising decrease (it should increase as particle size is decreased) of 7.22% in 109 days indicating the surface densification/removal of sharp surface corners/formation of large particles. SEM photographs indeed showed that samples exposed to biofield after 20 days showed increase in size as well as rounded corners. Thermal analysis indicated an increase in melting temperature by 9.9% in samples treated after 57 days along with a much reduced change in weight.
Comments: 4 Pages.
[v1] 2016-09-19 01:08:12
Unique-IP document downloads: 55 times
Vixra.org is a pre-print repository rather than a journal. Articles hosted may not yet have been verified by peer-review and should be treated as preliminary. In particular, anything that appears to include financial or legal advice or proposed medical treatments should be treated with due caution. Vixra.org will not be responsible for any consequences of actions that result from any form of use of any documents on this website.
Add your own feedback and questions here:
You are equally welcome to be positive or negative about any paper but please be polite. If you are being critical you must mention at least one specific error, otherwise your comment will be deleted as unhelpful.