Chitosan (CS) and sodium alginate (SA) are two widely popular biopolymers which are used for biomedical and pharmaceutical applications from many years. The objective of present study was to study the effect of biofield treatment on physical, chemical and thermal properties of CS and SA. The study was performed in two groups (control and treated). The control group remained as untreated, and biofield treatment was given to treated group. The control and treated polymers were characterized by Fourier transform infrared (FT-IR) spectroscopy, CHNSO analysis, X-ray diffraction (XRD), particle size analysis, differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). FT-IR of treated chitosan showed increase in frequency of –CH stretching (2925→2979 cm- 1) vibrations with respect to control. However, the treated SA showed increase in frequency of –OH stretching (3182→3284 cm-1) which may be correlated to increase in force constant or bond strength with respect to control. CHNSO results showed significant increase in percentage of oxygen and hydrogen of treated polymers (CS and SA) with respect to control. XRD studies revealed that crystallinity was improved in treated CS as compared to control. The percentage crystallite size was increased significantly by 69.59% in treated CS with respect to control. However, treated SA showed decrease in crystallite size by 41.04% as compared to control sample. The treated SA showed significant reduction in particle size (d50 and d99) with respect to control SA. DSC study showed changes in decomposition temperature in treated CS with respect to control. A significant change in enthalpy was observed in treated polymers (CS and CA) with respect to control. TGA results of treated CS showed decrease in Tmax with respect to control. Likewise, the treated SA also showed decrease in Tmax which could be correlated to reduction in thermal stability after biofield treatment. Overall, the results showed that biofield treatment has significantly changed the physical, chemical and thermal properties of CS and SA.
Comments: 9 Pages.
[v1] 2016-08-05 05:05:31
Unique-IP document downloads: 155 times
Vixra.org is a pre-print repository rather than a journal. Articles hosted may not yet have been verified by peer-review and should be treated as preliminary. In particular, anything that appears to include financial or legal advice or proposed medical treatments should be treated with due caution. Vixra.org will not be responsible for any consequences of actions that result from any form of use of any documents on this website.
Add your own feedback and questions here:
You are equally welcome to be positive or negative about any paper but please be polite. If you are being critical you must mention at least one specific error, otherwise your comment will be deleted as unhelpful.