Formulation of Porosity Calculation for Three-Dimension Granular Materials in the Case of Spherical Particles

Authors: Sparisoma Viridi, Supri jadi, Reza Rendian Septiawan

A derivation of formulation for calculating porosity of three-dimension granular materials is presented in this work, where granular particles are assumed spherical. Overlapping area problem is solved in two-dimension using geometry in two overlapping circles. The three-dimension overlap is formulated through numeric integration from the two dimension overlap.

Comments: 4 pages, 4 figures, technical report

Download: PDF

Submission history

[v1] 2015-03-26 02:19:25

Unique-IP document downloads: 45 times

Vixra.org is a pre-print repository rather than a journal. Articles hosted may not yet have been verified by peer-review and should be treated as preliminary. In particular, anything that appears to include financial or legal advice or proposed medical treatments should be treated with due caution. Vixra.org will not be responsible for any consequences of actions that result from any form of use of any documents on this website.

Add your own feedback and questions here:
You are equally welcome to be positive or negative about any paper but please be polite. If you are being critical you must mention at least one specific error, otherwise your comment will be deleted as unhelpful.

comments powered by Disqus